1. The longitudinal tear in the middle of the steel belt is 14-15 meters, how to repair it?
The upper and lower covering glue of the damaged part can be peeled off (the length exceeds the damaged part by 50-100mm, and the width exceeds the damaged part by 30-50mm), and at the same time, take a piece of rubber with the same size as the peeled part (preferably with a layer of cloth), and then It can be repaired according to the cold glue method.
2. Comparison of EP high temperature resistant belt and cotton canvas high temperature resistant belt:
a. The same point: the surface covering glue is the same.
b. Differences: cotton canvas can withstand a maximum temperature of 150 degree ; EP-TNG canvas can be used for a long time at 200 degree , and can be used at a maximum of 220 degree ;
The strength of cotton canvas is relatively low, only 50N/mm; while the strength of EP-TNG canvas is relatively high, and the commonly used type 200 is 200N/mm;
Die Haftung des hochtemperaturbeständigen Riemens aus Baumwollgewebe ist relativ gering, und die Haftung des hochtemperaturbeständigen EP-Riemens ist relativ hoch; Die Lebensdauer des hochtemperaturbeständigen EP-Riemens ist offensichtlich länger als die des hochtemperaturbeständigen Baumwollleinenriemens.
3. Hot glue stripping method (is it good to remove the glue at one end)?
Dies ist eine andere Art des Klebens, diese Methode ist auch möglich, aber wenn Sie diese Methode verwenden, beachten Sie die folgenden Punkte:
a. Be sure to use sealing glue;
b. The parts where the edge rubber parts meet must be connected by vulcanized rubber;
c. The parts where the rubber is connected must be polished
The disadvantage is that the edge glue part is easily damaged if it is not handled properly.
4. The joint temperature reaches 120 degree , but does not reach the normal vulcanization temperature?
no. The normal vulcanization and crosslinking temperature of rubber is determined by the vulcanizing agent and accelerator in the rubber. In order to ensure the safety of rubber processing, the general manufacturer will not set the vulcanization starting temperature of the rubber used in the conveyor belt to be very low. Therefore, when the temperature reaches 120 degree , the rubber will not enter the normal vulcanization state. Therefore, at 120 degree , the quality of the conveyor belt joint will be greatly affected.
Wenn die Vulkanisationstemperatur höher als die kritische Vulkanisationstemperatur des Beschleunigers und des Vulkanisationsmittels ist und die normale Vulkanisationstemperatur nicht erreichen kann, kann normalerweise das Verfahren zur Verlängerung der Vulkanisationszeit übernommen werden, damit die Vulkanisation des Kautschuks den Anforderungen entspricht. Im Allgemeinen verlängert sich die Vulkanisationszeit jedes Mal, wenn die Temperatur unter 10 Grad sinkt, um das 2--fache. Aus Leistungsgründen raten wir natürlich von der Verwendung von Nieder-temperatur und Langzeitvulkanisation ab.
5. Can core rubbers from different manufacturers be mixed?
Es wird nicht empfohlen, Kerngummis verschiedener Hersteller zu mischen, da die Rezeptur von Kerngummis verschiedener Hersteller unterschiedlich ist. Es gibt viele Arten von Compoundiermitteln in Gummi, und einige von ihnen haben interaktive Reaktionen. In der Rezeptur des gleichen Herstellers wird es keine Compoundierungsmittel mit unerwünschten Wechselwirkungen geben, aber die Rezepturen verschiedener Hersteller sind sehr unterschiedlich. Bei der Verwendung kann es zu interaktiven Reflexionen von Compoundiermitteln kommen, die den Gebrauchseffekt von Kerngummi beeinträchtigen.